TEROSON MS 939 white (290 ml)
Teroson® MS 939 – High-performance adhesive and sealant based on SMP for elastic joints
Documents
Internal reference:
62-939.KT.ML290
HS code:
35069190
- Teroson® MS 939 is a one-component, moisture-curing adhesive and sealant based on silane-modified polymers (SMP), specifically developed for high-strength and permanently elastic bonding and sealing applications. The product cures to form an elastic, stress-relieving material and is free of solvents, isocyanates, silicone, and PVC. Due to its thixotropic consistency, Teroson® MS 939 offers excellent sag resistance – ideal for vertical applications and overhead work.
- The excellent UV and weather resistance makes it suitable for both indoor and outdoor use. Thanks to its good paint compatibility and broad adhesion to metals, plastics, painted and powder-coated surfaces, Teroson® MS 939 is particularly versatile, for example in the automotive, HVAC, electrical, or plastics industries.
1-component SMP adhesive
Elastic and stress-relieving
Pasty and non-sagging, no slipping
Skin formation time: approx. 4–10 minutes
Curing speed: approx. 3 mm / 24 hrs.
Shore A hardness: approx. 55
Tensile strength: approx. 3.0 MPa
Elongation at break: approx. 250 %
Service temperature: –40 °C to +100 °C (briefly up to 120 °C)
UV- and weather-resistant, paintable
Solvent-free, silicone-free, and isocyanate-free
Shelf life: 12 months (at 10–25 °C)
Metals (e.g., steel, aluminum)
Plastics (e.g., ABS, GRP – after preliminary testing)
Powder-coated and painted surfaces
Sheet metal, painted body parts, Plexiglas®, polycarbonate
(*only after preliminary testing, risk of stress cracking)
Bonding of side panels and roof skins
Seals in vehicle and caravan construction
Use in container, wagon, and metal construction
Climate, ventilation, electrical, and plastics industry
Elastic interior and exterior seams
General apparatus and enclosure construction
Suitable materials:
Typical application areas:
Substrates must be clean, dry, and free of grease
Primer or mechanical roughening may be necessary
Processing temperature: +5 °C to +40 °C
Application is carried out with a hand or pneumatic caulking gun (290–570 ml cartridges)
Curing occurs through atmospheric moisture; higher temperatures and humidity accelerate the process
- Uncured adhesive can be removed with Cleaner+Thinner A or FL
Processing instructions:
Technical data for TEROSON MS 939 white (290 ml)
| Product Information | |
|---|---|
| Brand | Teroson |
| Technology | Silane-modified polymer (SMP) |
| Container | 290 ml |
| Consistency | Paste-like |
| Tensile Strength | 3 MPa |
| Temperature resistance | -40 °C to +100 °C (120 °C for short periods) |
| Further Properties | |
|---|---|
| UV resistance | Very good |
| Performance at Full Cure | |
|---|---|
| Elongation at break | 250 % |
| Physical Properties | |
|---|---|
| Color | white |
| Density | 1.5 g/cm³ |
| Skin formation time | 4-10 min |
| Hardness (Shore A) | 55 |
| General | |
|---|---|
| Components | 1K – moisture-curing |
| Curing rate | 3 mm / 24 h |
| Stress at 100% elongation | approximately 1.3 MPa |
| Volume change | < 2 % |
| Processing temperature | +5 °C to +40 °C |
Please refer to the technical data sheet (TDS) in the "Documents" tab for binding values.
No frequently asked questions are available for this product.
Your question not covered?
Our technical team provides personal advice on material selection, processing questions, and individual requirements. Fast and competent.
Product Specifications
| Product Information | |
|---|---|
| Brand | Teroson |
| Technology | Silane-modified polymer (SMP) |
| Container | 290 ml |
| Consistency | Paste-like |
| Tensile Strength | 3 MPa |
| Temperature resistance | -40 °C to +100 °C (120 °C for short periods) |
| Further Properties | |
|---|---|
| UV resistance | Very good |
| Performance at Full Cure | |
|---|---|
| Elongation at break | 250 % |
| Physical Properties | |
|---|---|
| Color | white |
| Density | 1.5 g/cm³ |
| Skin formation time | 4-10 min |
| Hardness (Shore A) | 55 |
| Uncategorized | |
|---|---|
| Components | 1K – moisture-curing |
| Curing rate | 3 mm / 24 h |
| Stress at 100% elongation | approximately 1.3 MPa |
| Volume change | < 2 % |
| Processing temperature | +5 °C to +40 °C |
| Keywords | |
|---|---|
| Keywords | |