- Brand
- Bonderite
- Container
- 1 kg
Product Description
Bonderite L-GP MS 401N is a yttrium oxide dispersion in solvent (DAG MS-401N) as a stop-off for titanium component manufacturing in the SPF/DB process — inert to titanium, low carbon inclusion, halogen-free.
Bonderite L-GP dry film lubricants from Henkel/Acheson — graphite, PTFE, MoS₂, or boron nitride dispersions that, after drying, form a tightly adhering film with a low coefficient of friction and release properties. L-GP MS 401N is tailored to specific industrial applications — the most important properties and areas of application are listed below.
Bonderite L-GP MS 401N (formerly DAG MS-401N) is a silver gas impact-resistant stop-off for titanium component manufacturing using the superplastic forming/diffusion bonding process. It contains yttrium oxide and a low-carbon binder in a solvent—inert to titanium, preventing alpha-case formation. Halogen-free and ready-to-use.
What distinguishes the L-GP MS 401N
What is the L-GP MS 401N used for?
Processing
Recommended accessories
L-GP MS 401N in comparison
Direct comparison with related Bonderite products from our range.
L-GP MS 401N Current Product |
L-GP BN 4479 FA → | L-GP BND60A → | L-GP 6013 → | |
|---|---|---|---|---|
| Technology | Yttrium oxide dispersion | Boron nitride dispersion | Refractory boron nitride coating | Carbon dispersion |
| Base material | Yttrium oxide + low-carbon binder | Crystalline boron nitride | Boron nitride | Carbon + thermoplastic resin |
| Carrier | Butyl glycol acetate | Solvent | Aerosol solvent | MIBK |
| Application | SPF-DB Stop-Off | Anti-diffusion barrier | High-temperature protection | Electrically conductive coating |
| Temperature range | High-temperature titanium | +1'000/+2'000 °C | +1'000 °C | Normal service |
| Main application | Titan-Stop-Off | Titanium SPF-DB | Welding nozzle protection | Capacitor paper |
Frequently asked questions about L-GP MS 401N
Practical application and design questions — answered by SILITECH.
Bonderite L-GP MS 401N: Yttrium oxide dispersion in solvent (DAG MS-401N) as a stop-off for titanium component fabrication using the SPF/DB process — inert to titanium, low carbon inclusion, halogen-free. Main applications: Titanium component fabrication SPF-DB, aerospace titanium structures, diffusion bonding stop-off.
After evaporation of the carrier (water, solvent, or MIBK), dry film lubricants form a firmly adhering lubricating film of solid lubricant (graphite, MoS₂, PTFE, or boron nitride). Advantages over liquid lubricants: no migration, lifelong lubrication in many applications, high-temperature suitability, substrate versatility (wood, metal, plastic, glass), electrically conductive possible (graphite) or highly insulating (boron nitride).
Store in the unopened original container in a dry, cool place — typically between +5 and +40 °C, exact values see TDS. Protect water-based products from frost. Consult the Safety Data Sheet (SDS) before use. Observe the expiry date on the packaging. Store aerosol sprays at low temperature and in a well-ventilated area.
In the comparison table above, you will find related Bonderite products with different properties — different carrier, different solid lubricant, different temperature range, or different application specialization. If you are unsure about the optimal choice, we will be happy to advise you — contact SILITECH with your specific application (substrate, temperature, load, processing workflow).